首页 > 产品资料 > 注塑铁氧体磁  
 


把钕铁硼合金粉末与树脂(PA12, PPS)，添加剂等混合后， 以注射成

形的方 式生产出来的磁体就是注塑钕铁硼磁石。 注塑钕铁硼具有体

积小，磁性能 高的优点，尤其是一些薄壁磁环， 复杂形状的精密磁

部件等，许多压制及 烧结钕铁硼无法达到的尺寸精度都能用注塑成

型生产。由于电机的发展越来 越趋向微细化，特别是无刷电机，对

尺寸，磁性能，稳定性等都有很高的要 求，因此注射成形钕铁硼磁

体最能满足这些条件。
 
Magnetic Characteristics & other physical characteristics of Injection Molded NdFeb Magnet- END series
EARTH MAGNETS-EPF- END Series
Test method
Unit
END-352K
END-372K
END-392K
END-502K
END-392C
END-502C
END-602C
END-702C
END-364
END-374
END-
1102
www.earthmagnets.com
Magnetic power
-
-
Nd-Fe-B alloy
Base resin
　
　
PA12
MAGNETIC PROPERTIES
-
-
Isotropic
Anisotropic
Residual flux densityBr
　
mT
450
490
540
590
550
590
640
680
450
500
720
Coercive forcebHc
　
kA/m
310
330
350
370
340
370
390
410
290
310
477
Intrinsic coercive forceiHc
　
kA/m
680
680
670
690
690
690
690
690
710
710
987
Maximum energy productBHmax
　
kJ/m3
36
42
48
56
49
56
64
72
36
40
90
Thermal coefficientΔBr/Br
　
%/℃
-0.1
-0.1
-0.1
-0.1
-0.1
-0.1
-0.1
-0.1
-0.1
-0.1
-0.1
Thermal coefficientΔHc/Hc
　
%/℃
-0.4
-0.4
-0.4
-0.4
-0.4
-0.4
-0.4
-0.4
-0.4
-0.4
-0.4
OTHER PROPERTIES
　
　
　
　
　
　
　
　
　
　
　
　
　
Tensile strength
ASTM D-638
MPa
46
42
40
37
45
43
37
35
42
35
-
Flexural strength
ASTM D-790
MPa
98
93
85
75
95
92
80
70
82
70
70
Flexural modulus
ASTM D-790
MPa
9500
12000
15000
17500
11000
12000
17500
19000
21000
22000
12859
Izod impact (with notch)
ASTM D-256
J/m
42
42
40
40
41
41
40
40
42
40
39
Rockwell hardness coefficient
ASTM D-785
R scale
105
108
110
110
108
110
110
110
117
120
108
Heat deflection temperature1.82Mpa
ASTM D-648
0 C
130
135
150
153
145
150
153
155
215
217
155
Specific gravity
ASTM D-792
-
4.7
5.0
5.4
5.7
5.0
5.4
5.7
5.9
4.6
5.0
5.3
Water absorption (230C 24 hrs in water)
ASTM D-570
%
0.06
0.05
0.04
0.04
0.04
0.04
0.04
0.04
0.01
0.01
-
Molding shrinkage coefficient　
DIC Method
%
0.5
0.5
0.5
0.4
0.5
0.4
0.4
0.4
0.4
0.4
0.4
Coefficient of thermal expansion
DIC Method
0 C
6.1X10-5
5.2X10-5
4.0X10-5
3.7X10-5
5.2X10-5
4.0X10-5
3.7X10-5
3.7X10-5
3.2X10-5
3.0X10-5
3.7X10-
5
Melt flow rate （2700C x 5 kg)  　
ASTM D-1238
g/10min
600
500
300
200
500
300
200
150
 -
 -
160
Melt flow rate （2700C x 10 kg)  　
ASTM D-1238
g/10min
 -
 - 
 -
 -
 -
 -
 -
 -
110
70
-